Synthesis of titanium dioxide nanobeits

中文

华中师范大学学报(自然科学版)

1000-1190

2006

40

2

213-216

10.19603/j.cnki.1000-1190.2006.02.019

武汉市重大项目纳米专项基金（20041003068）.

本校为第一机构

以工业制备氧化钛的中间产物(Ti(OH)4)为原料,在180～230℃的碱性条件(KOH溶液)下,采用压力热晶法成功制备出了带状TiO2纳米晶.X射线衍射(XRD)结果表明,制得的TiO2为锐钛矿结构.扫描电镜(SEM)和透射电镜(TEM)观察显示,TiO2纳米晶平均带宽为10～15 nm,长度为几十到几百微米左右.研究表明,原料的预处理和反应温度直接影响纳米晶的生长.前驱物pH 值为14,陈化时间为12 h,生成的纳米晶较长,形貌一致;随着温度的升高,产物的晶化程度增加.最后,对带状TiO2的形成机制也进行了讨论.

TiO2 nanobelts were successfully prepared by pressure-thermalcrystallization method in alkaline solution（KOH） at the temperature ranging from 180℃ to 230℃ using the medial product Ti（OH）4 as raw material, which obtained from the industrial synthesized process of TiO2. X ray diffraction（XRD） results showed that TiO2 was anatase structure; Scanning electron microscopy（SEM） and transmission electron microscopy（TEM） observations demonstrated the average width of TiO2 was 10～15 nm, with the lengths in the range of several tens to severa...